Fracture Properties of α– and ĸ–Al2O3 Hard Coatings Deposited by Chemical Vapor Deposition

Abstract

Although α– and κ–Al2O3 hard coatings deposited by chemical vapor deposition are well established in the metal-cutting industry for their ability to increase the performance and lifetime of cutting tools, the literature on their fracture properties is scarce. Thus, within this study, the microstructure and mechanical properties of α– and κ–Al2O3 coatings were investigated and compared to each other. X-ray diffraction and scanning electron microscopy combined with electron backscatter diffraction showed that both coatings exhibited a fiber texture, where the α-Al2O3 coating displayed a (0001) texture and the κ–Al2O3 coating a (001) texture with a certain (013) contribution. Higher hardness and Young’s modulus values of 31.0 ± 0.9 GPa and 474.6 ± 12.5 GPa, respectively, were obtained for the α–Al2O3 coating, compared to 24.2 ± 0.8 GPa and 356.8 ± 7.9 GPa for κ–Al2O3. While the α–Al2O3 coating exhibited a higher fracture stress of 8.1 ± 0.3 GPa (compared to 6.4 ± 0.6 GPa for κ–Al2O3), the κ–Al2O3 coating showed a higher fracture toughness of 4.4 ± 0.3 MPa*m1/2 (compared to 3.2 ± 0.3 MPa*m1/2 for alpha).