Study of the Effect of PGDA Solvent on Film Formation and Curing Process of Two-Component Waterborne Polyurethane Coatings by FTIR Tracking

Abstract

Waterborne polyurethane coatings were prepared using polyhydroxyacrylate dispersion, polyisocyanate, and propylene glycol diacetate (PGDA). The rate of reaction between hydroxyl and NCO groups in film formation and curing processes was studied by FTIR. The influence of PGDA amount on film formation and curing was also studied. Results showed that PGDA content had a significant effect on the curing process. With less than 10% PGDA, the role of PGDA was more to assist diffusion of polyhydroxyacrylate and polyisocyanate resin droplets. This promoted the reaction between hydroxyl groups and NCO. With more than 10% PGDA, its effect as a solvent was more and it inhibited the reaction between hydroxyl and NCO groups. When the amount of PGDA was about 10%, the synergy between both the roles promoted the crosslinking and curing reactions. The extent of the curing reaction of NCO was more than 70% in 4 h, which was significantly higher, compared with that of about 30% without PGDA. The good applicability and appearance of the waterborne polyurethane coating prepared in this study were verified for the application to carbon fiber metro vehicles.