The Influence of Salt Erosion on the Mechanical Performances of Ultra-High-Performance Concrete with Secondary Aluminum Dross

Abstract

Secondary aluminum dross containing a large amount of active substance can be used to prepare concrete. The mechanical strengths, the mass loss rate (MR) and the relative dynamic modulus of elasticity (RME) of ultra-high-performance concrete with secondary aluminum dross are researched. The NaCl freeze–thaw cycles (F-Cs) and dry–wet alternation (D-A) effects with NaCl and Na2SO4 are considered. The corresponding permeability of chloride ions and the carbonation depth (Dc) are obtained. The scanning electron microscope (SEM) photos are researched to reveal the variation of the mechanical mechanism. Results show that after specimens’ suffering from the action of 20 NaCl D-As, the MR of ultra-high-performance concrete is the highest. Specimens exposed to 200 NaCl F-Cs show the lowest MR and CMC. The RME of UHPC under salt actions increase in the order of 20 NaCl D-As < 20 Na2SO4 D-As < 200 NaCl F-Cs. After suffering 200 NaCl F-Cs, 20 Na2SO4 D-As and 20 NaCl D-As, the corresponding Dc values are 1.86 mm to 2.31 mm, 1.79 mm to 2.23 mm and 2.11 mm to 2.76 mm. The flexural strength decreases at the rates of 0.99%–25%, 3.92%–27.84% and 1.47%–21.59% respectively. The MR increases and the RME decreases as the cubic function changes with the amount of salt erosion. After the secondary aluminum dross is added, the CMC decreases at the rates of 0% to 11.53%, 0% to 33.17% and 0% to 8.41% during the process of the salt action. The SAD can reduce the Dc with the decreasing rates of 19.48%, 23.55% and 19.73%. The SAD can increase the compactness of ultra-high-performance concrete. Ultra-high-performance concrete suffering from 20 NaCl D-As shows the largest number and the highest width of cracks. However, when the specimens are exposed to 20 Na2SO4 D-As, the number of cracks is the lowest and the width is the narrowest.