The Effect of Curing Temperature and Thickness of Polybutyl Methacrylate Siloxane Coatings on the Corrosion Protection of Structural Steel S355

Abstract

This study aimed to determine the effects of coating thickness and curing temperature on the properties of a polybutyl methacrylate-siloxane coating deposited on structural steel S355. First, the thermal properties of the sol as a function of temperature were investigated using thermogravimetric analysis coupled with mass spectrometry and differential scanning calorimetry. After coating deposition on structural steel S355 using a dip-coating process, the coating composition and porosity were evaluated using Fourier transform infrared spectroscopy and photothermal beam deflection spectroscopy. In the second part, coating thickness, topography, and corrosion properties were studied as functions of withdrawal rate during deposition. The corrosion properties of variously prepared coatings were evaluated using electrochemical impedance measurements in 3.5 wt.% NaCl and salt spray testing according to the ASTM B117 standard. An elevated curing temperature (at 150 °C) of the polybutyl methacrylate siloxane sol-gel coating impairs greater crosslinking and lower porosity, while the optimal thickness of 4 μm is achieved with the appropriate withdrawal rate to obtain a homogeneous, defect-free surface. Under these optimal conditions, the protection of structural steel against corrosion in a chloride environment lasting for more than 6 months can be achieved.