Structural Modifications of Sodium Polyacrylate-Polyacrylamide to Enhance Its Water Absorption Rate

Abstract

Superabsorbent polymers (SAPs) can absorb a large amount of water and find broad applications in various industries. There are many reports on the synthesis and structural modification techniques to improve the water absorption property of SAPs. However, we see few studies on the comparison and integration of these techniques. In this study, three structurally modified SAPs were synthesized and are evaluated for the effects of surface cross-linking, foaming, and the integration of the two modifications to improve the absorption rate and capacity of a conventional SAP. First, sodium polyacrylate-polyacrylamide was prepared as the base polymer by the aqueous solution polymerization method. Second, the base polymer was modified with surface cross-linking to enhance absorption, and a surface cross-linked SAP was obtained. Third, the base polymer was modified with foaming to obtain a foamed SAP. Lastly, the foamed SAP was modified further with surface cross-linking to obtain a foamed and surface cross-linked SAP. In comparison with the base polymer, the three synthesized SAPs were evaluated for their absorption performance. Results show that their absorption performance could be improved by the three modification processes. Specifically, the surface cross-linked SAP had the best absorption capacity under load, the foamed SAP had the highest absorption capacity of 1954 g/g, and the foamed and surface cross-linked SAP had the fastest absorption rate with an initial swelling rate of Kis = 21.94.