Preparation of Copper-Doped Zinc Oxide (CZO) Nanoparticles and CZO/Acrylic Copolymer Emulsion with Polyvinylpyrrolidone (PVP) Coated on Glass Substrate for Optical Properties

Abstract

This study investigated the effect of copper (Cu) doping content on zinc oxide with varied weight percentages and the dispersion of Cu-doped ZnO (CZO) by adding polyvinylpyrrolidone (PVP), coated on a glass substrate, through a physical assessment and optical property and thermal insulation testing. CZO NPs were synthesized by using the sol–gel method with a zinc acetate precursor. The powder X-ray diffraction (XRD) patterns of the CZO showed that the solid solubility limit was below 5 mol% without a secondary phase. A field-emission scanning electron microscopy (FE-SEM) micrograph demonstrated that the particle size of CZO was in nanoscale with the packing of a quasi-spherical shape. The UV-Vis-NIR reflectance spectra of the powder showed that 1 mol% CZO has the highest near-infrared (NIR) reflectivity in the wavelength 780–2500 nm, with great visible light transmission. The CZO NPs were loaded in acrylic copolymer in different weight percentages ranging from 25 wt% to 75 wt%, the film thickness of the coating was varied from 5 µm to 100 µm, and PVP was added into this nanocomposite polymer to disperse through an ultrasonication method. The results showed that the highest loading of CZO powder in a polymer at 75 wt% in 100 µm of thickness with polyvinylpyrrolidone (PVP) as a dispersant showed better sample dispersion and retained good transparency to the naked eye.