The Synthesis of Nonionic Hyperbranched Organosilicone Surfactant and Characterization of Its Wetting Ability

Author:

Liu Jie,Zhang Fei Fei,Song Ying Hu,Lv Kun,Zhang Ni,Li Yan Chun

Abstract

In this research, the epoxy silicone oil and self-made hydroxyl-terminated hyperbranched polymer (HBP-OH) were used to synthesis the nonionic hyperbranched organosilicone surfactant (NHSi). The molar rate of hydroxyl groups of HBP-OH and epoxy groups of epoxy silicon oil (n-OH: n-epoxy) was adjusted from 5:1~60:1 to prepare a series of NHSi. The Gel Permeation Chromatography (GPC), Fourier Transform Infrared Spectroscopy (FT-IR), contact angle measuring instrument, surface tensiometer and Scanning Electron Microscope (SEM) were employed to characterize the structure and property of HBP-OH and NHSi. GPC analysis indicated that the Mn of HBP-OH was 340.5. FT-IR analysis showed that with the increase of molar rate of n-OH:n-epoxy, the peak intensity of –OH increased. The prepared NHSi was then used to prepare the water solution. The lowest surface tension of NHSi solution was 24.71 mN·m−1 when the n-OH:n-epoxy was 30:1 in the preparation process. The minimum water contact angle of waterborne polyurethane (WPU) emulsion by adding 2% of NHSi was 14.85° on the surface of glass. The wetting experiments showed that the NHSi has good wetting ability to fixed sea-island superfine fiber synthetic material.

Publisher

MDPI AG

Subject

Materials Chemistry,Surfaces, Coatings and Films,Surfaces and Interfaces

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3