Comparison of Sputtered and Evaporated Vanadium Pentoxide Thin Films for Resistive Microbolometer Application
Author:
Saeed NimraORCID, Akhtar SaadORCID, Hanif Muhammad BilalORCID, Hussain Sajid, Dogar Salahuddin, Zia-ur-Rehman , Bhatti Farrukh AzizORCID, Mosiałek MichałORCID, Napruszewska Bogna Daria, Motola MartinORCID, Khan Abdul FaheemORCID
Abstract
V2O5 thin films have made impressive progress in the development of resistive microbolometers. The challenging parameters for microbolometers are the active material selection and the deposition methods. It might be a more promising way to achieve a good performance of the devices. The present work deals with the V2O5 thin films fabricated on soda lime glass substrates by using e-beam evaporation and magnetron sputtering techniques at a substrate temperature of 200 °C. Afterward, samples were annealed at 300 and 400 °C for 1 h to obtain uniform and stoichiometric thin films. X-ray Diffraction (XRD) showed that the thin films deposited by magnetron sputtering were amorphous in nature, even after annealing at elevated temperatures; however, the thin films fabricated by the electron beam evaporation technique show crystalline nature, which was improved by annealing. XRD also revealed various mixed phases of VOx in electron beam-deposited films. Optical properties were determined using UV-Visible spectroscopy, which showed a decrease in transmittance from 81% down to 57% by increasing the annealing temperature. Similarly, the band gap calculated for electron beam evaporated and magnetron sputtered V2O5 thin films was observed in the range of 1.41 to 2.25 eV. Rutherford backscattering (RBS) was performed to determine the thickness and composition of the films. Slight variations have been observed in intended and deposited thicknesses of films fabricated by e-beam and sputtering techniques. Structural properties revealed by Field Emission Scanning Electron Microscope (FESEM) were found to be the uniform, compact and dense surface of the as-deposited and 300 °C annealed samples. However, annealing at 400 °C changed the surface morphology into nanorods in e-beam and plate-like structures in the sputtered film. EDS proved the elemental concentration of vanadium and oxygen in these V2O5 thin films. Electrical properties were investigated using the Hall measurement technique which showed better conductivity of sputtered films than e-beam deposited films. It can be concluded that the cost-effective and reliable microbolometers infrared (IR) sensors can be fabricated using annealed sputtered films.
Subject
Materials Chemistry,Surfaces, Coatings and Films,Surfaces and Interfaces
Reference27 articles.
1. Nanostructured multi-layer MgF2/ITO coatings prepared via e-beam evaporation for efficient electromagnetic interference shielding performance;Saleem;Appl. Surf. Sci.,2022 2. Cheema, D.A., Danial, M.O., Hanif, M.B., Alghamdi, A.S., Ramadan, M., Khaliq, A., Khan, A.F., Subhani, T., and Motola, M. (2022). Intrinsic properties and future perspective of HfO2/V2O2/HfO2 multi-layer thin films via e-beam evaporation as a transparent heat mirror. Coatings, 12. 3. Rehman, I., Hanif, M.B., Alghamdi, A.S., Khaliq, A., Halim, K.A., Subhani, T., and Khan, A.F. (2022). Intrinsic properties of multi-layer TiO2/V2O5/TiO2 coatings prepared via e-beam evaporation. Materials, 15. 4. Abrar, S., Hanif, M.B., Alghamdi, A.S., Khaliq, A., Abdel Halim, K.S., Subhani, T., and Khan, A.F. (2022). Synthesis and characterization of nanostructured multi-layer Cr/SnO2/NiO/Cr coatings prepared via e-beam evaporation technique for metal-insulator-insulator-metal diodes. Materials, 15. 5. Correlation between metal-insulator transition characteristics and electronic structure changes in vanadium oxide thin films;Ruzmetov;Phys. Rev. B,2008
|
|