Significant anisotropy in mechanical properties was observed in 316L stainless steel (SS) that was subjected to selective laser melting (SLM) to produce a hierarchical structure, composed of molten pool, columnar grains, and a cellular substructure. Such anisotropy was induced by the geometric relationship between the boundary of the molten pool and the tensile force. The in situ tensile test showed initial deformation rapidly occurred at the boundary of the molten pool, followed by strain localization, and a lower ductility was obtained when loaded in the longitudinal direction (perpendicular to the molten pool). By contrast, the deformation was significantly constrained because of the geometry of the boundary of the molten pool, and substantial deformation occurred in the cellular substructure during loading in transverse direction (parallel to the molten pool). Finally, the quantitative analysis revealed that the high-level strength was attributed to the high-density dislocations and the fine cellular substructure.
Funder
National Natural Science Foundation of China
Natural Science Foundation of Guizhou Province
One Hundred Person Project of Guizhou Province
Subject
General Materials Science,Metals and Alloys
Cited by
21 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献