Effect of Heating Process on Microstructure and Properties of 2205/Q235B Composite Interface

Author:

Xiao Fengqiang,Wang Dongpo,Gao Zhiming,Zhou Lanju

Abstract

In this paper, the influence of heating process parameters on interface characteristics and mechanical properties of 2205/Q235B clad steel plate was systematically studied. The results showed that the interfacial gap of the 2205/Q235B composite blank was completely bonded by the mutual diffusion of elements under the action of temperature and metallurgical bonding is achieved. The shear strength of the air-cooled samples was only 114–132 MPa, which was far lower than that of water-quenched samples and rolling deformation samples and was unable to meet the requirements of engineering applications. With the increase in heating temperature and holding time, the diffusion distance of the Cr element gradually increased. After rolling deformation, the diffusion distance of the Cr element was significantly reduced to 4.1–10.2 μm. Rolling deformation of the specimen in the decarburization showed the lowest microhardness, and in combination with the microhardness of the interface is about 236–256 HV, which is between the hardness of Q235B and 2205. The 2205 stainless-steel shows the lowest corrosion rate and the best corrosion resistance when rolling at 1200 °C. It was found that the corrosion was the most significant in the side of Q235B near the bonding zone. The corrosion pit width increased gradually with increased heating temperature.

Funder

Shandong Taishan industry leading talents project

Publisher

MDPI AG

Subject

General Materials Science,Metals and Alloys

Cited by 3 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3