Effect of Temperature on Corrosion Behavior of Laser-Remelted CrFeCoNi Coating

Author:

Wang Caimei,Yu Yang,Shao Minghao,Zhang Hua

Abstract

The CrFeCoNi coating was fabricated by the laser remelting method. The microstructure of the coating was detected. The corrosion behavior of coating at different temperatures was investigated by electrochemical measurements. Potentiodynamic polarization test results indicated that the corrosion current density increased with the increase in corrosion solution temperature in 3.5 wt% NaCl and 0.5 mol/L H2SO4 solutions, suggesting that the CrFeCoNi coating exhibited higher resistance to corrosion attack at lower solution temperature. The breakdown potential of the CrFeCoNi coating exhibited a decreasing trend with increasing solution temperature in 3.5 wt% NaCl solution. This indicated that the passive film formed at low temperatures had higher stability. The electrochemical impedance spectroscopy test indicated that the CrFeCoNi coating possessed higher charge transfer resistance at lower solution temperatures. The corrosion mechanisms of the coating at different temperatures were also revealed.

Funder

Cross Scientific Research Exploration Project of Beijing Institute of Petrochemical Technology

Beijing Science and Technology Plan Project

Publisher

MDPI AG

Subject

General Materials Science,Metals and Alloys

Cited by 2 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3