Abstract
The effect of friction stir welding on microstructure and corrosion property was studied in Fe-30Mn-3Al-3Si (wt.%) twinning-induced plasticity steel using both an electron backscattered diffractometer and electrochemical testing (i.e., polarization test and electrochemical impedance spectroscope). The stir zone has a relatively higher corrosion resistance with uniform dissolution on the surface despite after welding, whereas the base metal shows localized corrosion attack with deep and long degradation along the grain boundaries. This is due to the corrosion-resistant coincidence site lattice boundaries caused by discontinuous dynamic recrystallization via the grain boundary bulging during the friction stir welding.
Subject
General Materials Science,Metals and Alloys