Polygonal Pt nanoparticles were synthesized using ultrasonic spray pyrolysis (USP) at different precursor concentrations. Physicochemical analysis of the synthesized Pt particles involved thermogravimetric, microscopic, electron diffractive, and light absorptive/refractive characteristics. Electrochemical properties and activity in the oxygen reduction reaction (ORR) of the prepared material were compared to commercial Pt black. Registered electrochemical behavior is correlated to the structural properties of synthesized powders by impedance characteristics in ORR. The reported results confirmed that Pt nanoparticles of a characteristic and uniform size and shape, suitable for incorporation on the surfaces of interactive hosts as catalyst supports, were synthesized. It is found that USP-synthesized Pt involves larger particles than Pt black, with the size being slightly dependent on precursor concentration. Among ORR-active planes, the least active (111) structurally defined the synthesized particles. These two morphological and structural characteristics caused the USP-Pt to be made of lower Pt-intrinsic capacitive and redox currents, as well as of lower ORR activity. Although being of lower activity, USP-Pt is less sensitive to the rate of ORR current perturbations at higher overpotentials. This issue is assigned to less-compact catalyst layers and uniform particle size distribution, and consequently, of activity throughout the catalyst layer with respect to Pt black. These features are considered to positively affect catalyst stability and thus promote USP synthesis for improved properties of host-supported Pt catalysts.
Subject
General Materials Science,Metals and Alloys
Cited by
6 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献