Development of Hot-Wire Laser Additive Manufacturing for Dissimilar Materials of Stainless Steel/Aluminum Alloys

Abstract

The formation of brittle intermetallic compounds (IMCs) at the interface between dissimilar materials causes considerable problems. In this study, a multi-material additive manufacturing technique that employs a diode laser and the hot-wire method was developed for stainless steel/aluminum alloys. An Al-Mg aluminum alloy filler wire (JIS 5183-WY) was fed on an austenitic stainless-steel plate (JIS SUS304) while varying the laser power and process speed and using paste-type flux and flux-cored wire. The effects of laser power and process speed on phenomena during manufacturing and IMC formation were investigated. Finally, the wall-type multilayer specimens were fabricated under optimized conditions. The suppression of IMC formation to a thickness of less than 2 μm was achieved in the specimens, along with a high interfacial strength of over 120 MPa on average.