The Effects of Three Remineralizing Agents on the Microhardness and Chemical Composition of Demineralized Enamel

Author:

Salinovic Ivan,Schauperl Zdravko,Marcius Marijan,Miletic IvanaORCID

Abstract

This study aimed to determine the effects of three different varnish materials (containing casein phosphopeptide-amorphous calcium phosphate, nano-hydroxyapatite, and fluoride) on enamel. Thirty-three extracted human third molars were used for specimen preparation. These were demineralized using phosphoric acid. Three experimental groups (n = 11) were treated with 3M™ Clinpro™ White Varnish, MI Varnish®, and Megasonex® toothpaste, respectively, every twenty-four hours for fourteen days. Analysis of the microhardness of the specimens’ enamel surfaces was carried out via the Vickers method, and by scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDS). Analysis was performed at three stages: at baseline value, after demineralization, and after the period of remineralization. Data were subjected to Scheffe’s post hoc test. The mean microhardness values (HV0.1) obtained for the group of samples treated with MI Varnish® were higher compared with the other two groups (p = 0.001 for both comparisons), while the first and third groups did not differ significantly from each other (p = 0.97). SEM analysis showed uneven patterns and porosities on all samples tested. EDS results showed an increase in the mineral content of the examined samples, with the highest mineral content observed in the MI Varnish® group. It can be concluded that MI Varnish® use has a better remineralization effect on enamel than the other two materials.

Funder

Croatian Science Foundation

Publisher

MDPI AG

Subject

General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3