Mechanical and Microstructural Properties of Thermally Sprayed Metallic Materials in Compression Tests over a Vast Range of Strain Rates

Author:

Wypych Artur1ORCID,Jankowiak Tomasz2ORCID,Sumelka Wojciech2ORCID

Affiliation:

1. Institute of Materials Engineering, Poznan University of Technology, Jana Pawla II 24, 60-965 Poznan, Poland

2. Institute of Structural Analysis, Poznan University of Technology, Piotrowo 5, 60-965 Poznan, Poland

Abstract

This paper presents the mechanical behavior of thermally sprayed coatings produced using an arc wire coating material. The produced coatings were cut and subjected to strength resistance tests in static and in dynamic loading. The compressive behavior for the strain rates between 0.001 1/s and 2612 1/s was examined. The strain rate sensitivity of the material was recognized in the material during dynamic loading using the SHPB technique. Microstructural observations were made, and properties such as changes in porosity and the microhardness of the coatings tested were examined. A significant reduction in coating porosity was demonstrated after static loading (90%) and dynamic loading (86%). The result of porosity reduction is the strengthening of the coatings through an increase in the microhardness of these coatings after loading in the static test (160 HV 0.3/8) and the dynamic test (278 HV 0.3/8). As a result of the tests, the coatings retain their cohesion and remain consistent. At the same time, they can absorb a significant amount of mechanical energy due to plastic deformation and porosity reduction. The presented results concern a completely new coating material created from a core wire.

Funder

Poznań University of Technology

Publisher

MDPI AG

Subject

General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3