Fatigue Crack Arrest Induced by Localized Compressive Deformation

Author:

Barragán Edú R.,Ambriz Ricardo R.ORCID,Frutos José A.,García Christian J.,Gómora César M.,Jaramillo David

Abstract

The localized compressive deformation (LCD) effect generated by an indentation process at the crack tip on the fatigue crack growth of the 7075-T651 aluminum alloy is reported. Eccentrically loaded single-edge crack tension specimens (ESE(T)) were pre-cracked at a crack length of about 20 mm by applying a constant amplitude fatigue loading. Subsequently, the LCD process was performed by using a semi-spherical indenter with a radius of 16 mm to compress the crack tip zone at different forces (5.0, 7.0, 12.5, 13.5, 15.5 kN), applied on the opposite surfaces of the specimens. The fatigue cracking process was continued on the compressed samples until an overall crack length of about 30 mm was obtained. The compressive load and the number of delayed cycles is discussed in terms of crack length and crack tip opening displacement (CTOD). A direct relationship between the compressive force induced by the LCD process and the delay of the crack propagation due to the crack arrest was observed. This effect became evident at a compressive force of 5.0 kN, where the crack propagation was arrested for about 9000 cycles in comparison with the non-LCD sample. However, when the force increased, the crack arrest also increased. The crack was considered to be completely arrested at a compressive load of 15.5 kN, since the crack did not grow after the application of more than 3 × 106 cycles.

Publisher

MDPI AG

Subject

General Materials Science

Cited by 1 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3