Abstract
Analysis of dense Potassium Sodium Niobate (KNN) ceramic obtained by hot pressing (HP) method at 1100 °C are presented in this paper. The synthesis of KNN-based piezoelectrics meets the following challenges—low density of material, uncontrolled K/Na ratio, multiphase composition and formation of different KNN structures. The classical hot pressing approach results in contamination by carbon originating from graphite molds. The proposed hexagonal Boron Carbide (h-BN) layer between green sample and graphite mold could protect samples from carbon contamination. Additionally, the presence of h-BN may decrease the formation of oxygen vacancies, which allows us to maintain the semiconductor features of the KNN structure. Remaining issues were addressed with the addition of excess Na and Er2O3 doping. The results showed that excess Na addition allowed us to compensate evaporation of sodium during the synthesis and sintering. Er2O3 was added as sintering aid to limit abnormal grain growth caused by h–BN addition. The modification of amount of Na and Er2O3 addition resulted in high purity KNN samples with tetragonal structure and apparent density higher than 97%. Finally, piezoelectric features of prepared dense samples were measured and presented.
Subject
General Materials Science
Reference27 articles.
1. Piezoelectric Materials in Devices: Extended Reviews on Current and Emerging Piezoelectric Materials Technology and Applications;Setter,2003
2. Piezoelectricity of ferroelectric perovskites from first principles
3. Ferroelectric Ceramics: History and Technology
4. Ferroelectrics Devices;Uchino,2009
5. Review: environmental friendly lead-free piezoelectric materials
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献