Abstract
The aim of this study was to evaluate the persistence of alkaline hydrogels based on a common (N,N′-methylenebisacrylamide, BIS) and three recently published tetraallyl crosslinkers. Such hydrogels have been shown to be suitable materials for the rehabilitation of cementitious materials. Of the four crosslinkers under investigation, N,N,N′,N′-tetraallylpiperazinium dibromide decomposed quickly in 1 m KOH solution and was not considered further. BIS showed the first signs of a decomposition after several days, while tetraallylammonium bromide and N,N,N′,N′-tetraallyltrimethylene dipiperidine dibromide remained unaffected. In contrast to BIS, which suffers from low solubility in water, the two tetraallyl crosslinkers show unlimited miscibility with diallyldimethylammonium hydroxide solutions. For the study, gels with up to 50 wt % crosslinker were prepared. Of these, gels containing tetraallylammonium bromide always show the highest degrees of swelling, with a peak value of 397 g/g at a content of 2 wt %. Under accelerated ageing at 60 °C for 28 d, gels crosslinked with BIS ultimately turned liquid, while the storage modulus and the degree of swelling of the two tetraallyl-crosslinked gels remained unchanged. This indicates that alkaline gels can be suitable for long application periods, which are common for rehabilitation measures in the construction industry.
Funder
Federal Ministry of Education and Research
Subject
Polymers and Plastics,Organic Chemistry,Biomaterials,Bioengineering
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献