Abstract
Fe-25Cr-15Co (wt.%) permanent magnets were fabricated via selective laser melting (SLM) and in situ alloying from a blend of Fe, Cr and Co elemental powders. Under the optimal laser scanning process, the as-built Fe-25Cr-15Co alloy has a homogeneous composition distribution without defects such as holes or un-melted particles, and presents a single α phase with the bcc crystal structure. The density of as-built samples was 7.705 g/cm3 (the relative density is 99.32%). The preferred magnetic properties of the sample in the isotropic state were obtained as Hc = 22.84 kA/m, Br = 0.86 T and (BH)max = 7.98 kJ/m3. The hardness and yield strength of Fe-25Cr-15Co permanent magnets are above 331.5 HV and 800 MPa, respectively. The results of this study verified the feasibility of fabricating Fe-Cr-Co permanent magnets by SLM in situ alloying and can be extended to a wide range of applications that require complex shapes with variable magnetic circuit characteristics or gradient structures.
Funder
National Key Research and Development Program of China
Subject
General Materials Science,Metals and Alloys
Cited by
10 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献