Influence of Continuous Annealing Temperature on Mechanical Properties and Texture of Battery Shell Steel

Author:

Ning Beijia,Zhao ZhengzhiORCID,Mo Zhiying,Wu Hong,Peng Chong,Gong Honggen

Abstract

To study the influences of continuous annealing temperature on microstructure, mechanical properties and textures of battery shell steel, continuous annealing experiments were conducted at 710 °C, 730 °C, 760 °C and 780 °C respectively. The mechanical properties and normal anisotropy index (r) were measured by tensile test and the textures were investigated using the method of electron backscatter diffraction (EBSD). The results show that as annealing temperature rose, the grain size, fracture elongation and r value increased, whereas the strength and yield ratio decreased. The yield strength was 122 MPa, the tensile strength was 286 MPa, meanwhile the elongation and r value arrived at 38.8% and 2.3 when the annealing temperature rose to 780 °C. After annealing, the main texture in battery shell steel is {111} <112>, followed by {111} <110>. With the increase of annealing temperature, textures in {001} crystallographic plane weakened while textures in {111} plane strengthened, which is beneficial to the deep drawability of the steel.

Publisher

MDPI AG

Subject

General Materials Science,Metals and Alloys

Reference17 articles.

1. Research progress and application situation of steel for battery box of battery electric vehicles;Zhao;Hebei Metal.,2016

2. Non-metallic inclusion control technology for high quality cold rolled steel sheets;Wang;J. Iron Steel,2013

3. Ferritic steels

4. Discussion on typical surface defects of battery shell and their causes;Xue;Baosteel Tech.,2014

5. Texture analysis of tinplate steel and its application in production of double reduced high strength tinplate grades with controlled earing properties;černík;Mater. Sci. Eng.,2015

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3