Effect of Combined Addition of CeLa and GdY on Microstructure and Mechanical Properties of As-Cast Al-Cu-Mn Alloys

Abstract

In this study, the effects of the combined addition of CeLa and GdY on the microstructure and mechanical properties of as-cast Al-4Cu-1Mn alloys were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and tensile testing. The results show that the minor addition of CeLa and GdY leads to a refinement of grain size. The addition of CeLa results in the formation of supersaturated vacancies in the Al matrix, whereas the addition of GdY leads to a decrease in the precipitation temperature of the Al2Cu phase. The combined CeLa and GdY additions can significantly increase ultimate tensile strength (UTS) while losing only a small amount of elongation (EL). Compared with the unmodified alloy, the grain size and SDAS of the alloy (0.2 wt.% CeLa + 0.1 wt.% GdY) were diminished by 67.2% and 58.7%, respectively, while maximum hardness and UTS rose by 31.2% and 36.9%, respectively.