Relation between Mechanical Milling Parameters in Phase Transformation and Oxygen Content in Ti–Nb–Mo Powders for Posterior Sintering

Author:

Gouvea Eber de SantiORCID,Rossi Mariana CorreaORCID,Escuder Angel VicenteORCID,Afonso Conrado Ramos MoreiraORCID,Borrás Vicente AmigóORCID

Abstract

The influence of open vessels during milling for 12, 24, 40 and 60 h on microstructure homogeneity and oxygen content effect in the β Ti–Nb–Mo system microstructure were studied. The β phase increased with longer milling times and the strain hardening on particles was verified at 60 h when agglomeration was greater and was also noticed after 40 h in the continuous mode. Oxygen content dropped slightly until 40 h and increased after 60 h, a result linked with the observed hardening. For 40 h in the continuous mode, the oxygen content was noted near 12 h, 24 h and 40 h with high hardness values. For the sintered parts, the α phase and oxygen content significantly increased in all samples. Microhardness-sintered samples decreased compared to sample powders due to grain growth during the sintering. Bending strength was higher at 60 h with more oxygen and α phase content. After 40 h in the continuous mode, more suitable mechanical properties were reached because hardness and bending strength were closer to bone tissue, which was associated with strain hardening and a small crystallite size.

Funder

Spanish Ministerio de Economía y Competitividad

São Paulo Research Foundation

Publisher

MDPI AG

Subject

General Materials Science,Metals and Alloys

Cited by 1 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3