Preparation and Performance of Thermochromic and Self-Repairing Dual Function Paint Film with Lac Resin Microcapsules and Fluorane Microcapsules

Author:

Yan Xiaoxing,Zhao Wenting,Wang Lin

Abstract

Microcapsules with lac resin as the core material and urea-formaldehyde resin as the wall material were prepared by in situ polymerization, and then the lac resin microcapsules and fluorane microcapsules were added into a water-based primer or topcoat, respectively, to prepare water-based coatings with dual functions of thermochromic and self-repair. The effects of different methods of adding microcapsules on the optical properties, mechanical properties, self-repairing properties, and the aging resistance of water-based paint film were investigated, so as to prepare water-based paint film with the best discoloration and self-repairing functions. The results showed that the paint film with 10.0% fluorane microcapsules in the topcoat and 5.0% lac resin microcapsules in the primer had better comprehensive properties, and the paint film changed from yellow to colorless at 32 °C, with a color difference of 68.9, hardness of 3H, adhesion grade of 0, impact resistance of 13.0 kg∙cm, and elongation at break of 20.0%. The resistance of the paint film to NaCl, ethanol, and detergent was grade 2, with slight discontinuous marks, and the resistance to red ink was grade 3, with slight marks. The lac resin microcapsules have good aging resistance, which can enhance the aging resistance of the paint film with fluorane microcapsules. The gap width of the paint film was repaired by 2.1 µm, the self-repairing rate was 12.3%, and the paint film with lac resin microcapsules had a better crack inhibition effect. The results have provided a reference for multifunctional wood coatings.

Publisher

MDPI AG

Subject

Polymers and Plastics,General Chemistry

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3