Abstract
In this work, the development and application of multicomponents obtained from recycled polyethylene terephthalate (r-PET) waste and monotropic liquid crystals as anticorrosion coatings are reported. The r-PET raw material was alcoholyzed and reproduced as a thermoplastic polyester elastomer (TPEE) with different amounts (n%, n = 0, 1, 3, and 5) of 1,6-hexanediamine (HDA). Then, a fluorine-containing liquid crystal (4-cyano-3-fluorophenyl 4-ethylbenzoate (4CFE)) was incorporated into the TPEE mixture via solvent blending to modify and enhance the water resistance. The adhesion behavior of the coating on glass and iron substrates was evaluated by cross-cut tests and immersion tests in aqueous NaCl. In the corrosion resistance measurements, all of the coating samples fabricated with 10 ± 1 mm thickness were less active toward electrochemical corrosion (PEF% > 99%) than the bare iron plate, indicating that our work provided better protection against corrosion of the iron plate.
Funder
Ministry of Science and Technology, Taiwan
National Taipei University of Technology-Schezhen University Joint Research Program
Subject
Polymers and Plastics,General Chemistry
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献
1. Natural Dyes as Corrosion Inhibitors;Sustainable Textiles: Production, Processing, Manufacturing & Chemistry;2023
2. Efficacy of biomass-derived nanocomposites as promising materials as corrosion inhibitors;Antiviral and Antimicrobial Coatings Based on Functionalized Nanomaterials;2023