Effect of Core Architecture on Charpy Impact and Compression Properties of Tufted Sandwich Structural Composites

Abstract

This study presents a novel sandwich structure that replaces the polypropylene (PP) foam core with a carbon fiber non-woven material in the tufting process and the liquid resin infusion (LRI) process. An experimental investigation was conducted into the flatwise compression properties and Charpy impact resistance of sandwich composites. The obtained results validate an enhancement to the mechanical properties due to the non-woven core and tufting yarns. Compared to samples with a pure foam core and samples without tufting threads, the compressive strength increased by 45% and 86%, respectively. The sample with a non-woven layer and tufting yarns had the highest Charpy absorbed energy (23.85 Kj/m2), which is approximately 66% higher than the samples without a non-woven layer and 90% higher than the samples without tufting yarns. Due to the buckling of the resin cylinders in the Z-direction that occurred in all of the different sandwich samples during the compression test, the classical buckling theory was adopted to analyze the differences between the results. The specific properties of the weight gains are discussed in this paper. The results show that the core layers have a negative effect on impact resistance. Nevertheless, the addition of tufting yarns presents an obvious benefit to all of the specific properties.