Utilising Phosphogypsum and Biomass Fly Ash By-Products in Alkali-Activated Materials

Author:

Zhu Chengjie12ORCID,Pranckevičienė Jolanta1,Pundienė Ina1ORCID,Kizinievič Olga1

Affiliation:

1. Institute of Building Materials, Vilnius Gediminas Technical University, Linkmenų St. 28, 08217 Vilnius, Lithuania

2. College of Civil Engineering, Yancheng Institute of Technology, Xiwang Ave. 1, Yancheng 224051, China

Abstract

Significant environmental issues are raised by the phosphogypsum (PG) waste that is being produced. In Lithuania, about 1,500,000 tons of PG waste is generated yearly, and about 300 Mt is generated yearly worldwide. A by-product of burning wood biomass in thermal power plants is biomass fly ash (BFA). By 2035, compared to 2008 levels, industrial biomass incineration for combined heat and power and, as a consequence, BFA, is expected to triple. This study revealed the possibility of using these difficult-to-utilise waste products, such as BFA and PG, in efficient alkali-activated materials (AAM). As the alkaline activator solution (AAS), less alkaline Na2CO3 solution and Na2SiO3 solution were used. The study compared the physical–mechanical properties of BFA-PG specimens mixed with water and the AAS. After 28 days of curing, the compressive strength of the BFA-PG-based, water-mixed samples increased from 3.02 to 6.38 MPa when the PG content was increased from 0 to 30 wt.%. In contrast, the compressive strength of the BFA-PG-based samples with AAS increased from 8.03 to 16.67 MPa when the PG content was increased from 0 to 30 wt.%. According to XRD analysis, gypsum crystallisation increased when the PG content in the BFA-PG-based samples with water increased. The presence of AAS in the BFA-PG-based samples significantly reduced gypsum crystallisation, but increased the crystallisation of the new phases kottenheimite and sodium aluminium silicate hydrate, which, due to the sodium ions’ participation in the reactions, created denser reaction products and improved the mechanical properties. The outcome of this investigation aids in producing sustainable AAM and applying high volume of hardly usable waste materials, such as BFA and PG.

Publisher

MDPI AG

Subject

Management, Monitoring, Policy and Law,Renewable Energy, Sustainability and the Environment,Geography, Planning and Development,Building and Construction

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3