He Qianglong,Tian Tian,Tian Shi,Guo Wenchao,Shi Yunwei,Wang Aiyang,Wang Hao,Wang Weimin,Fu Zhengyi
Abstract
In this study, TiN–TiB2–hBN composite ceramics were prepared via reactive hot pressing using TiN and amorphous B powders as raw materials. Different sintering temperatures and composition ratios were studied. The results show that the 70 vol% TiN–17.6 vol% TiB2–12.4 vol% hBN ceramic composites obtained ideal comprehensive properties at 1600 °C. The relative density, Vickers hardness, bending strength, and fracture toughness were 99%, 11 GPa, 521 MPa, and 4.22 MPa·m1/2, respectively. Densification was promoted by the highly active reaction product TiB2, and the structural defects formed in the grains. Meanwhile, the good interfacial bonding between TiN and TiB2 grains and the uniform dispersion of ultrafine hBN in the matrix contributed to the excellent bending strength. Moreover, the toughening mechanism of crack deflection and grain pull-out improved the fracture toughness.
Funder
Fundamental Research Funds for the Central Universities
Sanya Science and Education Innovation Park of Wuhan University of Technology
Subject
General Materials Science
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献