An Experimental Study of the Tension-Compression Asymmetry of Extruded Ti-6.5Al-2Zr-1Mo-1V under Quasi-Static Conditions at High Temperature

Abstract

The tension-compression asymmetry (TCA) behavior of an extruded titanium alloy at high temperatures has been investigated experimentally in this study. Uniaxial tensile and compressive tests were conducted from 923 to 1023 K with various strain rates under quasi-static conditions. The corresponding yield stress and asymmetric strain hardening behavior were obtained and analyzed. In addition, the microstructure at different temperatures and stress states indicates that the extruded TA15 profile exhibits a significant yield stress asymmetry at different testing temperatures. The flow stress and yield stress during tension are greater than compression. The yield stress asymmetry decreases with the increase in temperature. The alloy also exhibits TCA behavior on the strain hardening rate. Its mechanical response during compression is more sensitive than tension. A dynamic recrystallization phenomenon is observed instead of twin generated in tension and compression under high-temperature quasi-static conditions. The grains are elongated along the tensile direction and deformed by about 45° along the compressive load axis. Finally, the TCA of Ti-6.5Al-2Zr-1Mo-1V (TA15) alloy is due to slip displacement. The tensile deformation activates basal <a>, prismatic <a> and pyramidal <c + a> slip modes, while the compressive deformation activates only prismatic <a> and pyramidal <c + a> slip modes.