Thermal Shock Performance of DBA/AMB Substrates Plated by Ni and Ni–P Layers for High-Temperature Applications of Power Device Modules

Author:

Choe Chanyang,Chen Chuantong,Noh SeungjunORCID,Suganuma Katsuaki

Abstract

The thermal cycling life of direct bonded aluminum (DBA) and active metal brazing (AMB) substrates with two types of plating—Ni electroplating and Ni–P electroless plating—was evaluated by thermal shock tests between −50 and 250 °C. AMB substrates with Al2O3 and AlN fractured only after 10 cycles, but with Si3N4 ceramic, they retained good thermal stability even beyond 1000 cycles, regardless of the metallization type. The Ni layer on the surviving AMB substrates with Si3N4 was not damaged, while a crack occurred in the Ni–P layer. For DBA substrates, fracture did not occur up to 1000 cycles for all kind of ceramics. On the other hand, the Ni–P layer was roughened and cracked according to the severe deformation of the aluminum layer, while the Ni layer was not damaged after thermal shock tests. In addition, the deformation mechanism of an Al plate on a ceramic substrate was investigated both by microstructural observation and finite element method (FEM) simulation, which confirmed that grain boundary sliding was a key factor in the severe deformation of the Al layer that resulted in the cracking of the Ni–P layer. The fracture suppression in the Ni layer on DBA/AMB substrates can be attributed to its ductility and higher strength compared with those of Ni–P plating.

Publisher

MDPI AG

Subject

General Materials Science

Cited by 24 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3