Epitaxial Lateral Overgrowth of {11-22} InGaN Layers Using Patterned InGaN Template and Improvement of Optical Properties from Multiple Quantum Wells

Abstract

We report the growth and characterization of thick, completely relaxed {11-22}-oriented InGaN layers using epitaxial lateral overgrowth (ELO). Although it was difficult to grow ELO-InGaN layers on patterned GaN templates, we succeeded in growing ELO-InGaN layers on a patterned InGaN template. The full width at half maximum of the X-ray rocking curve of ELO-InGaN on the InGaN templates was less than that of non-ELO InGaN. The photoluminescence intensity of InGaN/GaN multiple quantum wells on ELO-InGaN was approximately five times stronger than that on the {11-22} GaN template.