Abstract
In this study, single crystals of TrxBi2Se3 (Tr = Co, Fe, and Mn) were produced via a melt-grown reaction. All crystals are c-axis oriented with an excellent single crystalline phase. The smaller ionic radius of the transition metal elements makes the QLs of Bi2Se3 thinner. Their abundant magnetism will provide spin–phonon coupling channels when the phonons are scattering in the system. Both Stokes and anti-Stokes Raman spectroscopy were performed for the three optical phonon modes of the Bi2Se3 crystals. These peaks were centered at 74.5 cm−1, 133.4 cm−1, and 175.2 cm−1 and were attributable to the A1g(1), Eg(2), and A1g(2) modes, respectively. With an increase in the doping concentration, the magnetic and compressive strains induced by impurities dominate the phonon dynamics of materials. The results provide an effective scheme to regulate the thermoelectric properties of a Bi2Se3 system.
Funder
Sichuan Provincial Science and Technology Project
Nanchong Science and Technology Project
Enterprise Project
Sichuan Provincial Education Department Project
Subject
Inorganic Chemistry,Condensed Matter Physics,General Materials Science,General Chemical Engineering
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献