First Hydrogenation Enhancement in TiFe Alloys for Hydrogen Storage Doped with Yttrium

Abstract

The aim of this investigation was to improve the first hydrogenation of TiFe by adding yttrium. The compositions studied were TiFe + x wt.% Y with x = 4, 6, and 8. From electron microscopy it was found that all alloys were multiphase with a matrix of TiFe phase containing less than 0.4 at.% of Y and a secondary phase rich in yttrium. When x increased, the chemical compositions of the matrix changed and the secondary phase changed. The sample with 8% of yttrium had the fastest kinetics. The hydrogen capacity increased with the amount of Y.