Author:
Zuniga Luis,Gonzalez Gabriel,Orrostieta Chavez Roberto,Myers Jason C.,Lodge Timothy P.,Alcoutlabi Mataz
Abstract
We report results on the electrochemical performance of flexible and binder-free α-Fe2O3/TiO2/carbon composite fiber anodes for lithium-ion batteries (LIBs). The composite fibers were produced via centrifugal spinning and subsequent thermal processing. The fibers were prepared from a precursor solution containing PVP/iron (III) acetylacetonate/titanium (IV) butoxide/ethanol/acetic acid followed by oxidation at 200 °C in air and then carbonization at 550 °C under flowing argon. The morphology and structure of the composite fibers were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), and thermogravimetric analysis (TGA). These ternary composite fiber anodes showed an improved electrochemical performance compared to the pristine TiO2/C and α-Fe2O3/C composite fiber electrodes. The α-Fe2O3/TiO2/C composite fibers also showed a superior cycling performance with a specific capacity of 340 mAh g−1 after 100 cycles at a current density of 100 mA g−1, compared to 61 mAh g−1 and 121 mAh g−1 for TiO2/C and α-Fe2O3/C composite electrodes, respectively. The improved electrochemical performance and the simple processing of these metal oxide/carbon composite fibers make them promising candidates for the next generation and cost-effective flexible binder-free anodes for LIBs.
Funder
National Science Foundation
U.S. Department of Agriculture
Subject
Fluid Flow and Transfer Processes,Computer Science Applications,Process Chemistry and Technology,General Engineering,Instrumentation,General Materials Science
Cited by
26 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献