Abstract
The boiling performance of functionalized hybrid aluminum surfaces was experimentally investigated for water and self-rewetting mixtures of water and 1-butanol. Firstly, microstructured surfaces were produced via chemical etching in hydrochloric acid and the effect of the etching time on the surface morphology was evaluated. An etching time of 5 min was found to result in pitting corrosion and produced weakly hydrophilic microstructured surfaces with many microcavities. Observed cavity-mouth diameters between 3.6 and 32 μm are optimal for efficient nucleation and provided a superior boiling performance. Longer etching times of 10 and 15 min resulted in uniform corrosion and produced superhydrophilic surfaces with a micropeak structure, which lacked microcavities for efficient nucleation. In the second stage, hybrid surfaces combining lower surface energy and a modified surface microstructure were created by hydrophobization of etched aluminum surfaces using a silane agent. Hydrophobized surfaces were found to improve boiling heat transfer and their boiling curves exhibited a significantly lower superheat. Significant heat transfer enhancement was observed for hybrid microcavity surfaces with a low surface energy. These surfaces provided an early transition into nucleate boiling and promoted bubble nucleation. For a hydrophobized microcavity surface, heat transfer coefficients of up to 305 kW m−2 K−1 were recorded and an enhancement of 488% relative to the untreated reference surface was observed. The boiling of self-rewetting fluids on functionalized surfaces was also investigated, but a synergistic effect of developed surfaces and a self-rewetting working fluid was not observed. An improved critical heat flux was only obtained for the untreated surface, while a lower critical heat flux and lower heat transfer coefficients were measured on functionalized surfaces, whose properties were already tailored to promote nucleate boiling.
Funder
Javna Agencija za Raziskovalno Dejavnost RS
Ministry of Education, Youth and Sports of the Czech Republic
Subject
Process Chemistry and Technology,Chemical Engineering (miscellaneous),Bioengineering
Cited by
15 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献