Embrittlement Fracture Behavior and Mechanical Properties in Heat-Affected Zone of Welded Maraging Steel

Abstract

In welded maraging steels, mechanical properties, particularly ductility and toughness, are often compromised in the heat-affected zone (HAZ). This study focuses on 300-grade maraging steel bars, solution annealed at 1123 K for 1.5 h (5.4 ks) and welded using gas tungsten arc welding, followed by a post-weld heat treatment at 753 K for 13.33 h (48 ks). In situ observations during three-point bending tests on HAZ samples featuring coarsened prior austenite grain sizes were conducted to examine damage behavior and the crack path near the crack tip. The main crack initiated at the peak applied load during the bending test and, upon further loading, exhibited significant deflection and extension accompanied by numerous microcracks and localized crack branching. Distinctive damage features, such as transgranular cracking across block regions, intense intergranular cracking along packet boundaries with a pronounced shear component, and crowding of microcracks ahead of the crack tip, were observed in the HAZ sample during the in situ test. The interaction between the main crack tip and microcracks and its influence on the local crack propagation driving force was discussed using fracture mechanics. Experimental results, including tensile fracture surface observations and in situ images, along with analysis of the stress anti-shielding effect by microcracks, suggest that the HAZ sample exhibits embrittlement fracture behavior with lower ductility and toughness compared to the base metal sample.