Abstract
This paper focuses on the microstructure and tribological properties of novel hardfacing alloy based on Fe-C-Mn-B doped with Ni, Cr, and Si. The 4 mm-thick coating was deposited on the AISI 1045 carbon steel by the MIG-welding method using flux-cored wires in three passes. The transition zone thickness between the weld layers was ~80 μm, and the width of the substrate-coating interface was 5–10 μm. The following coating constituents were detected: coarser elongated M2B borides, finer particles of Cr7C3 carbides, and an Fe-based matrix consisting of ferrite and austenite. The nanohardness of the matrix was ~5–6 GPa, carbides ~16–19 GPa, and borides 22–23 GPa. A high cooling rate during coating fabrication leads to the formation of a fine mesh of M7C3 carbides; borides grow in the direction of heat removal, from the substrate to the friction surface, while in the transition zone, carbides become coarser. The dry sliding friction tests using a tribometer in PoD configuration were carried out at contact pressure 4, 7, 10, and 15 MPa against the AISI 1045 carbon steel (water-quenched and low-tempered, 50–52 HRC). The leading wear phenomenon at 4 and 7 MPa is fatigue, and at 10 and 15 MPa it is oxidation and delamination.
Funder
Ministry of Science and Higher Education
Key State Laboratory for Strength and Vibrations, Xi’an Jiaotong University
Subject
General Materials Science