Effect of Fabric Areal Weight on the Mechanical Properties of Composite Laminates in Carbon-Fiber-Reinforced Polymers

Author:

Andreozzi Marina1,Bianchi Iacopo1ORCID,Gentili Serena1,Mancia Tommaso1ORCID,Simoncini Michela1ORCID

Affiliation:

1. Department of Industrial Engineering and Mathematical Sciences, Università Politecnica delle Marche, Via Brecce Bianche 12, 60131 Ancona, Italy

Abstract

The present work aims at studying the effect of the reinforcing fabric areal weight on the mechanical properties of composite laminates in carbon-fiber-reinforced polymers. Three different pre-impregnated 2 × 2 twill weaves, characterized by the different areal weight values of 380, 630, and 800 g/m2 were used to produce laminates. These areal weights were selected to represent typical values used in structural application. A hand lay-up technique followed by an autoclave cycle curing was employed to produce the laminates. The desired final thickness of the laminates was obtained by laying-up a different ply number, as a function of the areal weight and thickness of each fabric. Uniaxial tensile and in-plane shear response tests were performed on samples obtained from laminates after curing. Furthermore, the presence of voids in composite materials were detected by performing resin digestion tests. Finally, light optical microscopy and stereomicroscopy analyses allowed observing the different arrangement of the plies in the cross-sections of laminates after curing and evaluating the degree of compaction as a function of the reinforcing fabric used. It was demonstrated that the fabric areal weight significantly affects the mechanical performances of the composite laminates; specifically, the decrease in the areal weight of the twill weave leads to an increase in tensile strength, elastic modulus, and in-plane shear stress, i.e., of about 56.9%, 26.6%, and 55.4%, respectively, if 380 g/m2 and 800 g/m2 fabrics are compared. These results are crucial for an optimal material selection during the design process for industrial applications and help to better understand composite material behavior.

Publisher

MDPI AG

Subject

Engineering (miscellaneous),Ceramics and Composites

Cited by 5 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3