Yang Bao,Wang Minglin,Zhang Hui,Liu Shuai,Wang Guobin,Wang Xuebing
Abstract
Heavy reduction (HR) is an effective technique to control V segregation in continuous casting bloom, but the effect of segregation improvement is limited by the parameters such as reduction position and reduction amounts. In order to improve the macrosegregation of bloom, numerical simulation and plant experiments are adopted in this research. A heat transfer model and a reduction model with comprehensive thermo-physical parameters were established. The two models were verified by comparing the measured surface temperature and the theoretical strain at the solidification front. It is determined that the position of the HR of the bearing steel bloom is 20.82 m~24.97 m from the meniscus, and the solid fraction in the center of the bloom is 0.6~1. The total reduction of the HR is set to 30 mm, and the reduction of each roller in the reduction range is set to 4 mm, 5 mm, 9 mm, 7 mm, and 5 mm, respectively, to prevent the formation of internal cracks. Plant trials were conducted to verify the effect of the optimized HR. The results show that the carbon segregation degree on the V channel and non-channel of the bloom decreases from 1.2 to 1.16 and increases from 0.93 to 0.95, respectively, and the central carbon segregation degree decreases from 1.17 to 1.15. Meanwhile, the internal crack was not found in the bloom.
Subject
General Materials Science,Metals and Alloys
Reference49 articles.
1. Effect of self-tempering on fatigue crack growth of heavy rail steel;Cen;Mater. Rep.,2021
2. Formation mechanism and control of semi-micro-segregation in rail steel bloom;Li;Iron Steel,2021
3. Simulation of the macrosegregation in the gear steel billet continuous casting process;Wang;Chin. J. Eng.,2021
4. Zhai, Y.Y., Li, Y., Yan, C., and Zhang, Y. Computational Prediction Model of Macrosegregation in Continuously Casting Steel Blooms. Proceedings of the Second International Conference on Digital Manufacturing & Automation.
5. Application of swirling flow nozzle and investigation of superheat dissipation casting for bloom continuous casing;Sun;Ironmak. Steelmak.,2016
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献