Effect of Two Brands of Glaze Material on the Flexural Strength and Probability of Failure of High Translucent Monolithic Zirconia

Abstract

(1) Background: The effect of glazing on the mechanical properties of monolithic high translucent zirconia is not well reported. Therefore, the purpose of this study was to evaluate the effect of glazing on the flexural strength of high translucent zirconia; (2) Methods: Ninety specimens were prepared from second-generation 3Y-TZP high translucent blocks and divided into three groups. Glaze materials were applied on one surface of the specimen and subjected to a four-point bending test and flexural stress and flexural displacement values were derived. Descriptive fractographic analysis of surfaces was conducted to observe the point of failure and fracture pattern.; (3) Results: Control-nonglazed (647.17, 1σ = 74.71 MPa) presented higher flexural strength values compared to glaze I (541.20, 1σ = 82.91 MPa) and glaze II (581.10, 1σ = 59.41 MPa). Characteristic strength (σƟ) from Weibull analysis also observed higher (660.67 MPa) values for the control specimens. Confocal microscopy revealed that glazed surfaces were much rougher than control surfaces. Descriptive fractographic analysis revealed that there was no correlation between the point of failure initiation and flexural strength; (4) Conclusions: The test results demonstrated that glazing significantly decreased the flexural strength and flexural displacement of the zirconia specimens.