Research on Atomic Oxygen Erosion Influence of Structural Damage and Tribological Properties of Mo/MoS2-Pb-PbS Thin Film

Abstract

To investigate atomic oxygen effects on tribological properties of Mo/MoS2-Pb-PbS film and further enlarge application range, atomic oxygen exposure tests were carried out for 5 h, 10 h, 15 h, and 20 h by the atomic oxygen simulator with atomic oxygen flux of 2.5 × 1015 atoms/cm2·s. The exposure time in test was equivalent to the atomic oxygen cumulative flux for 159.25 h, 318.5 h, 477.75 h, and 637 h at the height of 400 km in space. Then, the vacuum friction test of Mo/MoS2-Pb-PbS thin film was performed under the 6 N load and 100 r/min. By SEM, TEM, and XPS analysis of the surface of the film after atomic oxygen erosion, it was observed that atomic oxygen could cause serious oxidation on the surface of Mo/MoS2-Pb-PbS film, and the contents of MoS2, PbS, and Pb, which were lubricating components, were significantly reduced, and oxides were generated. From AES analysis and the variation in the main element content, Mo/MoS2-Pb-PbS thin film showed self-protection ability in an atomic oxygen environment. Hard oxide generated after atomic oxygen erosion such as MoO3 and Pb3O4 could cause the friction coefficient slight fluctuations, but the average friction coefficient was in a stable state.