Carbide precipitation and coarsening are investigated for quenched Dievar steel during tempering. Lath/lenticular martensite, retained austenite, lower bainite, auto-tempered, and larger spherical carbides are all observed in the as-quenched condition. The carbide precipitation sequence on tempering is ascertained to be: M8C7 + cementite → M8C7 + M2C + M7C3 → M8C7 + M7C3 + M23C6 → M8C7 + M7C3 + M23C6 + M6C; carbides become coarser on tempering, and the sizes for inter-lath carbides increase noticeably with increasing tempering temperatures due to the faster grain boundary diffusion, whereas the sizes for intra-lath carbides remain nearly constant. The rate of coarsening for carbides by tempering at 650 °C is much higher than those by tempering at 550 °C and 600 °C, due to the faster diffusion of alloying elements at higher temperatures.
Funder
Industry Prospects and Key Technology Competition Projects of JiangSu Province
Subject
General Materials Science
Cited by
14 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献