Abstract
Poly(butylene terephthalate-co-tetramethylene ether glycol) (PBT-co-PTMEG) copolymers with PTMEG ranging from 0 to 40 wt% were synthesized through melt polymerization. The structure and composition were supported by Fourier-transform infrared spectroscopy (FT-IR) and nuclear magnetic resonance spectroscopy (1H NMR). All samples had excellent thermal stability at a Td−5% around 370 °C. Crystallization temperature (Tc) and enthalpy of crystallization (ΔHc) were detected by differential scanning calorimetry (DSC), revealing a decrement from 182.3 to 135.1 °C and 47.0 to 22.1 J g−1, respectively, with the increase in PTMEG concentration from 0 to 40 wt%. Moreover, nonisothermal crystallization was carried out to explore the crystallization behavior of copolymers; the crystallization rate of PBT reduced gradually when PTMEG content increased. Hence, a decrement in the spherulite growth rate was detected in polarizing light microscope (PLM) observation, observing that the PTMEG could enhance the hindrance in the molecular chain to lower the crystallinity of PBT-co-PTMEG copolyester. Moreover, thermal properties and the crystallization rate of PBT-co-PTMEG copolymers can be amended via the regulation of PTMEG contents.
Funder
Ministry of Science and Technology, Taiwan
Subject
Polymers and Plastics,General Chemistry
Reference77 articles.
1. Thermoplastic copolyester elastomers;Djonlagic,2011
2. Thermoplastic elastomeric (TPE) materials and their use in outdoor electrical insulation;Amin;Adv. Mater. Sci.,2011
3. Modification of road bitumens with thermoplastic polymers
4. Thermoplastic elastomers: Fundamentals and applications;Richard J;Colloid Interface Sci.,2000
5. Thermoplastic elastomers;Holden,1987
Cited by
14 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献