Preparation of Li2S-AlI3-LiI Composite Solid Electrolyte and Its Application in All-Solid-State Li-S Battery

Author:

Anh Tu Tran12ORCID,Phuc Nguyen Huu Huy12ORCID,Anh Luong Thi Quynh12,Toan Tran Viet12

Affiliation:

1. Faculty of Materials Technology, Ho Chi Minh City University of Technology (HCMUT), 268 Ly Thuong Kiet Str., Dist. 10, Ho Chi Minh City 70000, Vietnam

2. Vietnam National University Ho Chi Minh City, Linh Trung Ward, Thu Duc Dist., Ho Chi Minh City 70000, Vietnam

Abstract

Novel (80Li2S − 20AlI3)·yLiI composite solid electrolytes (y = 5, 10, 15) were prepared by mechannochemical synthesis. XRD results showed that the pattern of 80Li2S − 20AlI3 was similar to that of AlI3, which means that Li2S was dissolved in AlI3 matrix during preparation. This structure was still maintained after LiI addition. The current measured at constant applied DC voltage indicated that (80Li2S − 20AlI3)·yLiI composites are intrinsically pure Li-ion conductors. The ionic conductivity at 25 °C of y = 10 was about 2.3 × 10−4 Scm−1, which was about three times higher than that of y = 0. The conductivity of y = 10 increased 20 times to 2.2 × 10−3 Scm−1 at 70 °C. These values were highest among those observed from Li2S-based materials. It was revealed that Li-ion moves in 80Li2S − 20AlI3 by a hoping mechanism, while the lattice dipoles are the origin of Li-ion movement in (80Li2S − 20AlI3)·yLiI. The polarization measurements using Liǀ90 (80Li2S − 20AlI3)·10LiI ǀLi and LiǀLi6PS5Clǀ90 (80Li2S − 20AlI3)·10LiIǀLi6PS5ClǀLi cells proved that 90 (80Li2S − 20AlI3)·10LiI reacts with Li metal, but it is relatively stable at a low voltage. Sample y = 10 was also employed as a solid electrolyte in the positive electrode of a solid-state Li-S battery to study its stability in the voltage range of the positive electrode. CuS and Li4.4Si were the electrode-active materials. The cell was cycled in CC-CV mode at 1.0 mA cm−2 (CC) with a cut-off voltage of 1.0–2.3 V. The cell delivered a stable capacity of about 400 mAh g−1CuS after 40 cycles.

Publisher

MDPI AG

Subject

Electrical and Electronic Engineering,Electrochemistry,Energy Engineering and Power Technology

Cited by 2 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3