Experimental Investigation on the Effects of Mineral Water Composition on the Leaching of Cement-Based Materials

Author:

Pouyanne Alienor12,Boudache Sonia12,Hilloulin Benoît1ORCID,Loukili Ahmed12,Roziere Emmanuel1ORCID

Affiliation:

1. Nantes Université, Ecole Centrale Nantes, Centre National de la Recherche Scientifique (CNRS), Civil Engineering and Mechanics Research Institute (GeM), Unité Mixte de Recherche (UMR) 6183, 44000 Nantes, France

2. Edycem, Parc d’Activité Vendée Sud Loire, Rue du Fléchet, 85600 Montaigu, France

Abstract

The common phenomenon observed for concrete in aggressive water is leaching, which involves the dissolution of cement hydration products. Many studies have focused on leaching in demineralised water or acid attacks, but mineral water still deserves further investigation. In most standards, the aggressiveness of a given water body is determined by its pH and not its composition. The effect of the calcium content of the water on degradation is yet to be determined. In this paper, the leaching of Portland cement-based mortar was induced by two types of drinking water with different calcium contents and buffer capacity in controlled conditions. The Langelier saturation index (LSI) was used to describe water aggressiveness based on the calco-carbonic equilibrium. The studied waters had the same pH but LSIs of +0.5 and −1.0 corresponding to scaling with respect to aggressive water; demineralised water was used as a reference. Microstructural damage was checked by TGA and X-ray microtomography. Macroscopic measurements were used to monitor global degradation. The soft water caused a 53% deeper deterioration of the mortar sample than the hard water. Soft water-induced leaching was found to be similar yet slower to leaching via demineralised water (with a mass loss of −2.01% and −2.16% after 200 days, respectively). In contrast, hard water induced strongly time-dependent leaching, and the damage was located close to the surface. The roughness of leached specimens was 18% higher in hard water than in soft water. The formation of calcite on the sample surface not only affects the leaching rate by creating a protective surface layer, but it could also act as a calcium ion pump.

Funder

EDYCEM

Publisher

MDPI AG

Cited by 1 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3