Reactive Sintering of Al2O3–Y3Al5O12 Ceramic Composites Obtained by Direct Ink Writing

Abstract

The main goal of this work was to obtain dense Al2O3–Y3Al5O12 ceramic composites by reactive sintering of three-dimensional samples, built by direct ink writing from a paste containing a mixture of Al2O3 and Y2O3 powders. To obtain a ceramic ink with proper rheological properties for extrusion-based printing, highly pure Al2O3 and Y2O3 powders in a percentage–weight ratio of 64:36 was mixed with 0.2 wt% MgO in a total solid loading of 42 vol% in aqueous media, adding carboxymethyl cellulose and polyethyleneimine solution as additives. The dried printed samples were sintered at final temperatures in the range of 1550 °C and 1650 °C; thus, relative densities of 83.7 ± 0.8%, 95.4 ± 0.4%, and 96.5 ± 0.5% were obtained for 1550 °C, 1600 °C, and 1650 °C, respectively. Rietveld refinement performed on the X-ray diffraction patterns indicated the presence of Al2O3 (42 to 47%) and Y3Al15O12 (58 to 61%) as crystalline phases, while micrographs showed the presence of equiaxial micrometric grains with average sizes of 1.8 ± 0.6 μm, for both phases and all sintering conditions. Samples sintered at 1600 °C and 1650 °C presented similar average Vickers hardness values of 14.2 ± 0.27 GPa and 14.5 ± 0.25 GPa, respectively. A slight increase in fracture toughness as sintering temperature increases was also stated, consistent with the densification.