Chinese Paulownia wood has been extensively used in the construction of timber buildings and lightweight sandwich structures. However, the bending and shear behaviors at elevated temperatures were not well understood. A total of 162 specimens were tested to investigate the bending, tangential shear, and radial shear performances of Chinese Paulownia wood under temperatures from 20 to 220 °C. It was found that the bending specimens exhibited ductile failure due to the progressive damage after reaching the peak load, while the tangential and radial shear specimens exhibited brittle shear failure along the shear plane. The elevated temperatures had limited effects on the failure modes. Under the same temperature, the retention rate of the modulus of elasticity is significantly higher than that of the modulus of rupture. Moreover, the bending strength, tangential shear strength, and radial shear strength generally and nonlinearly decreased with the increasing temperature. The EN 1995-1-2 design curve for the shear strength of wood at elevated temperatures is conservative for both the tangential and radial shear specimens. However, the design curve may not be adopted to estimate the tangential shear strength at temperatures higher than 220 °C.
Funder
National Natural Science Foundation of China
Postgraduate Research & Practice Innovation Program of Jiangsu Province
Subject
Polymers and Plastics,General Chemistry
Reference33 articles.
1. Fire performance of pultruded wood-cored GFRP sandwich components for building construction;Zhang;Case Stud. Constr. Mater.,2022
2. Fire resistance of unprotected cross-laminated timber floor panels: Parametric study and simplified design;Menis;Fire Saf. J.,2019
3. Gaff, M., Čekovská, H., Bouček, J., Kačíková, D., Kubovský, I., Tribulová, T., Zhang, L., Marino, S., and Kačík, F. (2021). Flammability Characteristics of Thermally Modified Meranti Wood Treated with Natural and Synthetic Fire Retardants. Polymers, 13.
4. Review and analysis of fire resistance tests of timber members in bending, tension and compression with respect to the Reduced Cross-Section Method;Schmid;Fire Saf. J.,2014
5. Fire resistance of cross-laminated timber panels loaded out of plane;Fragiacomo;J. Struct. Eng.,2013
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献