Phosphorylated Metal–Organic Framework for Reducing Fire Hazards of Poly(Methyl Methacrylate)

Abstract

The low fire safety performance (flame retardant and antistatic properties) of poly(methyl methacrylate) (PMMA) has severely limited practical applications. Here, a phosphorylated Zn-based metal–organic framework (ZIF-8-P) is employed as an effective flame retardant and antistatic agent to reduce the fire risk of PMMA. Encouragingly, the as-prepared PMMA/ZIF-8-P composite demonstrated not merely better mechanical properties (e.g., a rise of ca. 136.9% and 175.0% in the reduced modulus and hardness; a higher storage modulus), but also efficient fire safety properties (e.g., lower surface resistance; a decrease of ca. 73.1% in the peak heat release rate; a lower amount of total pyrolysis products), surpassing those of pure PMMA and a PMMA/ZIF-8 composite without phytic acid modification. Mechanism analysis is conducted to reveal the critical role of catalytic charring, char reinforcing, and the dilution of nonflammable gases from ZIF-8 additives during the combustion and pyrolysis process. Our study paves a promising way to achieve high performance PMMA composites.