Phase Stability and Transport Properties of (ZrO2)0.91−x(Sc2O3)0.09(Yb2O3)x Crystals (x = 0–0.01)

Abstract

Phase stability and transport properties of (ZrO2)0.91−x(Sc2O3)0.09(Yb2O3)x crystals (x = 0–0.01) have been studied before and after air annealing at 1000 °C for 400 h. The crystals have been grown by radio frequency (RF) heating in a cold crucible. The microstructure, phase composition, and electrical conductivity of the crystals have been studied using optical microscopy, X-ray diffraction, Raman spectroscopy, and impedance spectroscopy. Phase stability and degradation of ionic conductivity of the crystals upon long-term high-temperature heat treatment have been discussed. We show that the stabilization of ZrO2 co-doped with 9 mol.% Sc2O3 and 1 mol.% Yb2O3 provides transparent uniform crystals with the pseudocubic t″ phase structure having high phase stability. Crystals of this composition had the highest conductivity in the entire temperature range. Long-term high-temperature annealing of these crystals did not lead to conductivity degradation.