Bleached bamboo pulp, as a kind of natural cellulose, has received significant attention in the field of biomass materials due to its advantages of environmental protection and the abundance of raw materials. Low-temperature alkali/urea aqueous system is a green dissolution technology for cellulose, which has promising application prospects in the field of regenerated cellulose materials. However, bleached bamboo pulp, with high viscosity average molecular weight (Mη) and high crystallinity, is difficult to dissolve in an alkaline urea solvent system, restraining its practical application in the textile field. Herein, based on commercial bleached bamboo pulp with high Mη, a series of dissolvable bamboo pulps with suitable Mη was prepared using a method of adjusting the ratio of sodium hydroxide and hydrogen peroxide in the pulping process. Due to the hydroxyl radicals being able to react with hydroxyls of cellulose, molecular chains are cut down. Moreover, several regenerated cellulose hydrogels and films were fabricated in an ethanol coagulation bath or a citric acid coagulation bath, and the relationship between the properties of the regenerated materials and the Mη of the bamboo cellulose was systematically studied. The results showed that hydrogel/film had good mechanical properties, as the Mη is 8.3 × 104 and the tensile strength of a regenerated film and the film have values up to 101 MPa and 3.19 MPa, respectively. In this contribution, a simple method of a one-step oxidation of hydroxyl radicals to prepare bamboo cellulose with diversified Mη is presented, providing an avenue for a preparation of dissolving pulp with different Mη in an alkali/urea dissolution system and expanding the practical applications of bamboo pulp in biomass-based materials, textiles, and biomedical materials.
Funder
National Natural Science Foundation of China
Key Research and Development Program of Jiangxi Province
Major Science and Technology Project of Jiangxi Province “The Open Competition Mechanism to Select the Best Candidates”
Subject
Polymers and Plastics,General Chemistry
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献